ebalta AH 140 is a very thin liquid two-component-epoxy resin with high values of strength and high heat resistance. Due to its very good impregnating and wetting properties it is suitable as laminating resin for high-strength components with fabrics of glass -or carbon fiber. Especially for thin laminates, a post-curing of 16 hours at 80°C, after curing at room temperature, is essential in order to guarantee a complete curing. Otherwise the non post-cured laminate will be brittle and the adhesion of the layers with each other will not be sufficient. Applications Hand laminating Vacuum infusion carbon fibre sight laminates Laminates for boatbuilding Laminates for automotive industry Laminates for aeronautic Properties unfilled very thin liquid long processing time high heat resistance high strength excellent wet-out characteristics&&

About

ebalta AH 140 is a very thin liquid two-component-epoxy resin with high values of strength and high heat resistance. Due to its very good impregnating and wetting properties it is suitable as laminating resin for high-strength components with fabrics of glass -or carbon fiber. Especially for thin laminates, a post-curing of 16 hours at 80°C, after curing at room temperature, is essential in order to guarantee a complete curing. Otherwise the non post-cured laminate will be brittle and the adhesion of the layers with each other will not be sufficient. Applications Hand laminating Vacuum infusion carbon fibre sight laminates Laminates for boatbuilding Laminates for automotive industry Laminates for aeronautic Properties unfilled very thin liquid long processing time high heat resistance high strength excellent wet-out characteristics&&

Product Description
Generic	环氧树脂
Material Status	Commercial: Active
Features	Good Rigidity,High Heat Resistance
Availabilitys	Africa & Middle East ,North America,Asia Pacific,Europe

Technical Data
IMPACT	Nominal value	Unit	Test method
Charpy Unnotch Impact strength	30 to 46	kJ/m²	ISO 179

Uncured Properties	Nominal value	Unit
Density
20℃	1.10 to 1.14	g/cm³
viscosity
25℃	0.35 to 0.50	Pa·s
Curing time
20℃	48 to 72	hr
storage stability
20 ℃	90 to 110	min

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	84 to 90		ISO 7619
Bending modulus	2600 to 3200	MPa	ISO 178
bending strength	115 to 135	MPa	ISO 178
compressive strength	105 to 125	MPa	ISO 604

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	107 to 113	℃	ISO 75-2/B
Glass transition temperature	114	℃	TMA
Thermosetting components
resin	按重量计算的混合比: 100
Hardening method	按重量计算的混合比: 32
Post curing time
60℃	4.0 to 6.0	hr
80℃	5.0 to 6.0	hr
120℃	4.0	hr

Notes
1. Typical properties: these are not to be construed as specifications.
2. 200 g
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.