| About |
|---|
| EBA ALCUDIA® PA-303 is a copolymer suitable for blown film applications with good optical and mechanical properties even at low temperatures. The material has very good sealing properties. The butyl acrylate content is 3%. TYPICAL APPLICATIONS Shrink film Silage film Heavy-duty bags Recommended melt temperature 180°C. Processing characteristics of PA-303 are similar to LDPE and conventional polyethylene extruders are recommended.&& |
| Product Description | |
|---|---|
| Supplier | REPSOL |
| Generic | EBA |
| Material Status | Commercial: Active |
| Features | Good heat sealing,Food contact compliance |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.30 | g/10min | ISO 1133 |
| Butyl acrylate composition | 3.0 | wt% | |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 130 | µm | |
| tensile strength | |||
| MD, fracture, 130 µ m, blow molded film | 25.0 | MPa | |
| TD, fracture, 130 µ m, blow molded film | 25.0 | MPa | |
| Tensile strain | |||
| MD, fracture, 130 µ m, blow molded film | 500 | % | |
| TD, fracture, 130 µ m, blow molded film | 700 | % | |
| Drop hammer impact | |||
| 130 µ m, blow molded film | 600 | g | ISO 7765-1 |
| Elmandorf tear strength | |||
| MD: 130 µ m, blow molded film | 4.0 | N | |
| TD: 130 µ m, blow molded film | 6.0 | N |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 125 µ m, blow molded film | 70 | ASTM D2457 | |
| Haze | |||
| 125 µ m, blow molded film | 10 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |