| About |
|---|
| Ecodear® V911X51 is a Polylactic Acid (PLA) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Applications of Ecodear® V911X51 include appliances and business/office goods. Characteristics include: Flame Rated Eco-Friendly/Green&& |
| Product Description | |
|---|---|
| Supplier | Toray |
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Renewable resources,HB |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.21 | g/cm³ | |
| Melt Flow Rate | 28 | g/10min | ISO 1133 |
| Shrinkage rate | 0.40 to 0.60 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| 23℃ | 90.0 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 4.0 | % | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 3700 | MPa | ISO 178 |
| bending strength | |||
| 23℃ | 125 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 2.0 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 75.0 | ℃ | ISO 75-2/B |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 1.50 mm | HB | UL 94 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Sink-float Method |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |