| ecoflex® F Blend C1200 is our biodegradable, statistical, aliphatic-aromatic copolyester based on the monomers 1,4-butanediol, adipic acid and terephthalic acid in the polymer chain. ecoflex® F Blend C1200 will biodegrade to the basic monomers 1,4-butanediol, adipic acid and terephthalic acid and eventually to carbon dioxide, water and biomass when metabolized in the soil or compost under standard conditions. ecoflex® F Blend C1200 has properties similar to PE-LD because of its high molecular weight and its long chain branched molecular structure.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PCTG |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Aromatic,Good Printability,Biodegradable,Food contact compliance,Hypocrystalline,Aliphatic series,High molecular weight,Good Tensile Strength,Compostable,Welding,Branched polymer structure,Heat Stabilized |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 to 1.27 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.7 to 4.9 | g/10min | ISO 1133 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 2.50 to 4.50 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 32 | ISO 868 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 50 | µm | |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | 36.0 | MPa | ISO 527-3 |
| TD, fracture, 50 µ m, blow molded film | 45.0 | MPa | ISO 527-3 |
| MD, 50 µ m, blow molded film | 35.0 | MPa | ISO 527-3 |
| TD, 50 µ m, blow molded film | 44.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 50 µ m, blow molded film | 560 | % | ISO 527-3 |
| TD, fracture, 50 µ m, blow molded film | 710 | % | ISO 527-3 |
| Oxygen transfer rate | |||
| 23 ℃, 0% RH, 50 µ m, blow molded film | 1200 | cm³/m²/24 hr | ASTM D3985 |
| Water vapor transmittance | |||
| 23 ℃, 85% RH, 50 µ m, blow molded film | 140 | g/m²/24 hr | ASTM F1249 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| A50 | 91.0 | ℃ | ISO 306/A50 |
| Melting temperature | |||
| DSC | 110 to 120 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | |||
| 50.0 µ m, blow molded film | 82.0 | % | ASTM D1003 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Destruction energy | |||
| Dyna Test，50.0 µm | 240 | J/cm | DIN 53373 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |