| About |
|---|
| BFX303 is biodegradable compound for blown film. The Base material of BFX303 is PLA(Polylactic Acid). The film made by BFX303 will be stiff in comparison with PBAT-based film, and it will have good modulusin maintaining the shape.&& |
| Product Description | |
|---|---|
| Supplier | WooSung |
| Generic | PLA |
| Material Status | Commercial: Active |
| Features | Biodegradable |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 to 1.26 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 20 to 40 | g/10min | ASTM D1238 |
| water content | |||
| 105℃，10 min | < 1000 | ppm | Internal Method |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| MD, yield, 30 µ m, blow molded film | 37.6 | MPa | Internal Method |
| Tensile strain | |||
| MD，断裂，30 µm，吹塑薄膜 | 290 | % | Internal Method |
| Heat sealing strength | |||
| 30.0 µm | 10 | N | Internal Method |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| tear strength | |||
| 1mm notch，30 µm | 87.2 | kN/m | Internal Method |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown Film |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |