EcoLon® MRGF1616-BK

About
40% Mineral/Glass-Reinforced Nylon Resin (PA6)&&

Product Description
SupplierWellman
GenericPA6
Material StatusCommercial: Active
AvailabilitysNorth America,Latin America,Asia Pacific,Europe
Process MethodsInjection Molding

Technical Data
PHYSICALNominal valueUnitTest method
Density1.50g/cm³ISO 1183
Shrinkage rate ISO 294-4
TD:23℃0.70 to 1.1%ISO 294-4
MD:23℃0.20 to 0.60%ISO 294-4

MECHANICALNominal valueUnitTest method
tensile strength
Yield, 23 ℃105MPaISO 527-2
Tensile strain
Yield, 23 ℃2.0%ISO 527-2
Bending modulus
23℃9200MPaISO 178
bending strength
23℃155MPaISO 178

IMPACTNominal valueUnitTest method
Impact strength of cantilever beam notch
23℃6.0kJ/m²ISO 180

THERMALNominal valueUnitTest method
Hot deformation temperature
1.8 MPa, unannealed200ISO 75-2/A
Melting temperature
DSC220ISO 3146

Process Conditions
injectionNominal valueUnitTest method
Drying temperature79°C
Drying time2.0 to 4.0hr
Recommended maximum moisture content0.20%
Barrel rear temperature277 to 293°C
Barrel middle temperature271 to 282°C
Barrel front temperature266 to 277°C
Nozzle temperature254 to 282°C
Processing (melt) temperature271 to 299°C
Mold temperature71 to 93°C
Injection pressure34.5 to 138MPa
Back pressure0.345MPa
Screw speed30 to 120rpm

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.