| About |
|---|
| EM40010 is semi-crystalline biodegradable, aliphatic bio-polyester designed for use in sheet applications. EM40010 is PHA base compound with PLA, minerals and some additives. EM40010 is certificated to meet EN13432 & ASTM D6400 standards for biodegradable plastics. Typical applications: Cosmetics packaging, credit cards, thermoforming sheet&& |
| Product Description | |
|---|---|
| Supplier | Ecomann |
| Generic | PHA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good surface appearance,Renewable resources,Biodegradable,Moisture resistance,Hypocrystalline,Aliphatic series,Compostable,Heat Resistance, Good,Good coloring |
| Availabilitys | Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.32 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 170℃，2.16kg | 4.0 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| balance | < 0.40 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 30.0 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 5.0 | % | ASTM D638 |
| Bending modulus | 1400 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | 3.00 | kJ/m² | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 105 | ℃ | ASTM D1525 2 |
| Melting temperature | 140 to 160 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Yellowness index | 50 | YI | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 | °C | |
| Drying time | 3.0 | hr | |
| Barrel 1 zone temperature | 145 to 155 | °C | |
| Barrel 3 zone temperature | 150 to 160 | °C | |
| Barrel 5 zone temperature | 150 to 165 | °C | |
| Nozzle temperature | 155 to 165 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |