| About |
|---|
| EM50010 is semi-crystalline biodegradable, aliphatic bio-polyester designed for use in elastomer applications. EM50010 is PHA based compound with plasticizer and some additives. Ecomann EM50010 meets USFDA and EU direct food contact and OK compost and OK Home compost requirements. Typical applications: Pen cap, replace soft PVC, TPU, and thermo plastic elastomer&& |
| Product Description | |
|---|---|
| Supplier | Ecomann |
| Generic | PHA |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Good surface appearance,Low to No Fogging,Flame Characteristics,High Heat Resistance |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.20 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 170℃，2.16kg | 5.0 | g/10min | ASTM D1238 |
| Water absorption rate | |||
| balance | < 0.40 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Notched impact strength of cantilever beam | 无断裂 | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 50.0 | ℃ | ASTM D1525 2 |
| Melting temperature | 90.0 to 110 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Yellowness index | 60 | YI | Internal Method |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 30 | ISO 868 | |
| tensile strength | 5.00 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 600 | % | ASTM D638 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 60 | °C | |
| Drying time | 3.0 | hr | |
| Temperature at the rear of the barrel | 90 to 105 | °C | |
| Temperature in the middle of the barrel | 95 to 115 | °C | |
| Front temperature of material barrel | 95 to 120 | °C | |
| Nozzle temperature | 100 to 120 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Rate B (120°C/h), Loading 1 (10 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |