| (ECONAMID 6G35FLH) Polyamide 6, 35% glass fiber reinforced, heat stabilized, for injection moulding&& |
| Product Description | |
|---|---|
| Supplier | DOMO |
| Generic | PA6 |
| Material Status | Commercial: Active |
| Features | Heat Stabilized |
| Availabilitys | North America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.41 | g/cm³ | |
| Shrinkage rate | |||
| TD：23℃，72 hrs | 0.70 to 0.90 | % | |
| MD：23℃，72 hrs | 0.20 to 0.40 | % | |
| Viscosity number | |||
| 96% H2SO4 | 135 | cm³/g | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 6.5 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| 23℃ | 45 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| Notched impact strength of cantilever beam | |||
| 23℃ | 40 | kJ/m² |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 215 | ℃ | |
| 1.8 MPa, unannealed | 205 | ℃ | |
| Vicat Softening Temp | 210 | ℃ | |
| Melting temperature | 221 | ℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | |
| Volume resistivity | 1.0E+15 | ohms·cm |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 0.80 mm | HB | ||
| Burning rate | < 100 | mm/min |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| ISO Shortname | PA6,M,14-100,GF35 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 122 | ||
| Tensile modulus | 10000 | MPa | |
| tensile strength | |||
| fracture | 145 | MPa | |
| Tensile strain | |||
| fracture | 2.5 | % | |
| Bending modulus | 8500 | MPa | |
| bending strength | 210 | MPa |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 75 to 85 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Processing (melt) temperature | 240 to 270 | °C | |
| Mold temperature | 90 to 100 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 50% RH |
| 3. 0.079 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |