| About |
|---|
| Product Description | |
|---|---|
| Generic | PA56 |
| Material Status | Commercial: Active |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Relative viscosity | 2.72-2.80 | ||
| Moisture content | ≤2000 | ppm | |
| Nitrogen-containing group | 49-55 | mmol/kg | |
| granularity | |||
| section | 1 | g/100Pellets | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| Yield, 48h/23 ℃/50% RH | 82.6 | MPa | ISO 527 |
| Tensile strain | |||
| Fracture, 48h/23 ℃/50% RH | 5.1 | % | ISO 527 |
| Bending modulus | |||
| 48h/23℃/50%RH | 2680 | MPa | ISO 178 |
| bending strength | |||
| 48h/23℃/50%RH | 118 | MPa | ISO 178 |
| Rockwell hardness | |||
| Level L | 106 | ISO 2039-2 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 48h/23℃/50%RH | 6.2 | kJ/m² | ISO 180 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| melting point | |||
| 48h/23℃/50%RH | 254 | ℃ | ISO 11357 |
| Vicat Softening Temp | |||
| 48h/23℃/50%RH | 219 | ℃ | ISO 306 |
| Hot deformation temperature | |||
| 48h/23℃/50%RH | 74 | ℃ | ISO 75 |
| Process Conditions | |||
|---|---|---|---|
| Processing technology | Nominal value | Unit | Test method |
| drying temperature | 105 | ℃ | |
| Drying time | 4 | hrs | |
| Pre processing moisture content | ≤2000 | ppm | |
| Melting temperature | 260-290 | ℃ | |
| Nozzle temperature | 260-290 | ℃ | |
| Front third zone temperature | 250-290 | ℃ | |
| Front Second Zone Temperature | 250-290 | ℃ | |
| Front first zone temperature | 220-260 | ℃ | |
| Mold temperature | 70-90 | ℃ | |
| Back pressure | 0.3-0.7 | MPa | |
| Screw speed | 20-100 | rpm | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |