| About |
|---|
| Product Description | |
|---|---|
| Material Status | Commercial: Active |
| Features | No antimony,Laser welding,Low smoke,V-0,Flame Characteristics,Heat Stabilized,Low warping |
| Availabilitys | Latin America,North America,Europe,Africa & Middle East |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.67 | g/cm³ | ISO 1183/A |
| Water absorption rate | 0.02 | % | ISO 62 |
| Mold shrinkage rate | |||
| MD | 0.3 | % | ISO 294-4 |
| TD | 0.6 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | 120 | ISO 2039/2 | |
| tensile elongation | 185 | MPa | ISO 527-2/-1 |
| Tensile strain | |||
| fracture | 1.7 | % | ISO 527-2/-1 |
| Bending modulus | 13300 | MPa | ISO 178 |
| bending strength | 265 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 8.1 | kJ/m² | ISO 179/1eA |
| Charpy Unnotch Impact strength | |||
| 23℃ | 38 | kJ/m² | ISO 179/1eU |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 265 | ℃ | ISO 75-2/Af |
| Melting temperature | 280 | ℃ | ISO 11357 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flammability level | UL 94 | ||
| 3.2 mm | V-0 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| Injection | Nominal value | Unit | Test method |
| drying temperature | 130 | °C | |
| Drying time | 4.0 | hrs | |
| Processing (melt) temperature | 280 to 330 | °C | |
| Mold temperature | 130 to 150 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |