| About |
|---|
| ecovio® F2341 is our biodegradable product containing renewable resources. It is basically a compound of our biodegradable, statistical, aliphatic-aromatic copolyester ecoflex® and a small amount of polylactic acid (PLA). Due to its outstanding mechanical strength ecovio® F2341 offers a great down gauging potential needed for very thin film applications like T-shirt bags, organic waste bags etc.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PCTG |
| Material Status | Commercial: Negative |
| Features | Good Rigidity,Excellent Processability,Renewable resources,Aromatic,Biodegradable,Food contact compliance,Hypocrystalline,Aliphatic series,Good melt strength,Compostable,Welding,Heat Stabilized |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.36 to 1.40 | g/cm³ | ISO 1183 |
| Apparent density | 0.80 | g/cm³ | ISO 60 |
| Melt Volume Rate | |||
| 190℃，5 kg | 5.00 to 11.0 | cm³/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Tensile modulus | ISO 527-3 | ||
| MD, 25 µ m, blow molded film | 260 | MPa | ISO 527-3 |
| TD, 25 µ m, blow molded film | 130 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, 25 µ m, blow molded film | 25.0 | MPa | ISO 527-3 |
| TD, 25 µ m, blow molded film | 25.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 480 | % | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 570 | % | ISO 527-3 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 250 | g | ASTM D1709-A |
| Elmandorf tear strength | ISO 6383-2 | ||
| MD: 25 µ m, blow molded film | 1.3 | N | ISO 6383-2 |
| TD: 25 µ m, blow molded film | 0.90 | N | ISO 6383-2 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | DSC | ||
| — | 110 to 120 | ℃ | DSC |
| — | 140 to 155 | ℃ | DSC |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. ecoflex® |
| 3. PLA |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |