| About |
|---|
| ecovio® T 2308 is a biodegradable film product containing renewable resources. It is basically a compound of our biodegradable copolyester ecoflex® and polylactic acid (PLA). Because of the PLA content ecovio® T 2308 consists of 80% of renewable resources. PLA is the continuous phase in the structure of ecovio® T 2308 transferring the beneficial properties of ecoflex® into the new product.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PCTG |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Renewable resources,Good Printability,Biodegradable,Food contact compliance,Hypocrystalline,Good melt strength,Compostable,Heat Stabilized |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.24 to 1.26 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 190℃，5 kg | 7.50 to 11.5 | cm³/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | ISO 527-3 | ||
| MD，1000 µm | 2680 | MPa | ISO 527-3 |
| TD，1000 µm | 2240 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 1000 µ m | 27.0 | MPa | ISO 527-3 |
| TD, fracture, 1000 µ m | 20.0 | MPa | ISO 527-3 |
| MD，1000 µm | 56.0 | MPa | ISO 527-3 |
| TD，1000 µm | 40.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 1000 µ m | 56 | % | ISO 527-3 |
| TD, fracture, 1000 µ m | 38 | % | ISO 527-3 |
| Water vapor transmittance | |||
| 1000 µm | 3.8 | g/m²/24 hr | ASTM F1249 |
| Oxygen transfer rate | |||
| 1.00 mm | 32 | cm³/m²/bar/24 hr | ASTM D3985 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | |||
| B50 | 55.0 | ℃ | ISO 306 |
| Melting temperature | DSC | ||
| — | 110 to 120 | ℃ | DSC |
| — | 140 to 155 | ℃ | DSC |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Renewable Content | > 80 | % |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |