| Product Description | |
|---|---|
| Supplier | SKC |
| Material Status | Commercial: Negative |
| Availabilitys | North America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ASTM D792 |
| Mold shrinkage rate | 0.3 – 0.4 | % | ASTM D955 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 860 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.455 MPa, unannealed | 91 | ℃ | ASTM D648 |
| 1.820 MPa, unannealed | 77 | ℃ | ASTM D648 |
| 0.455 MPa, unannealed | 96 | ℃ | ASTM D648 |
| 1.820 MPa, unannealed | 80 | ℃ | ASTM D648 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Transmittance | 87 | % | ASTM D1003 |
| Haze | < 2.0 | % | ASTM D1003 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| R-level | ＞115 | ASTM D785 | |
| tensile strength | |||
| yield | 47 | MPa | ASTM D638 |
| fracture | 59 | MPa | ASTM D638 |
| yield | 46 | MPa | ISO 527 |
| fracture | 48 | MPa | ISO 527 |
| Tensile strain | |||
| yield | 6.4 | % | ASTM D638 |
| fracture | 245 | % | ASTM D638 |
| yield | 6.3 | % | ISO 527 |
| fracture | 200 | % | ISO 527 |
| bending strength | |||
| 74 | MPa | ASTM D790 | |
| 69 | MPa | ISO 178 | |
| Bending modulus | |||
| 1780 | MPa | ASTM D790 | |
| 1800 | MPa | ISO 178 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |