| About |
|---|
| Product Description | |
|---|---|
| Supplier | SKC |
| Generic | PETG |
| Material Status | Commercial: Active |
| Features | Transparency,Good transparency |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Specific Gravity | 1.23 | ASTM D792 | |
| Molding shrinkage | 0.3-0.4 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | >115 | R Scale | ASTM D-785 |
| Tensile Strength | |||
| Yield yld | 49 | MPa | ASTM D638 |
| Broken BRK | 55 | MPa | ASTM D638 |
| Yield yld | 47 | MPa | ISO 527-2 |
| Broken BRK | 48 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield yld | 6.6 | % | ASTM D882 |
| Broken BRK | 285 | % | ASTM D882 |
| Yield yld | 6.5 | % | ISO 527 |
| Broken BRK | 238 | % | ISO 527 |
| Flexural Strength | |||
| 72 | MPa | ASTM D790 | |
| 66 | MPa | ISO 178 | |
| Flexural Modulus | |||
| 1690 | MPa | ASTM D790 | |
| 1670 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 860 | J/m | ASTM D256 | |
| 93 | KJ/m² | ISO 180/1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature HDT | |||
| 0.45 MPa | 99 | ℃ | ASTM D648 |
| 1.82 MPa | 86 | ℃ | ASTM D648 |
| 0.45 MPa | 97 | ℃ | ISO 75-1/-2 |
| 1.82 MPa | 82 | ℃ | ISO 75-1/-2 |
| OPTICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Haze | <1.0 | % | ASTM D1003 |
| Transmittance | 84 | % | ASTM D1003 |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |