| About |
|---|
| Edgetek™ ATC-25GF/000 Natural UV是一种聚甲醛（POM）共聚物产品,含有的填充物为25% 玻璃纤维增强材料。 它可以通过注射成型进行加工,在欧洲有供货。 主要特性为:阻燃/额定火焰。&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | Copolymer Polyformaldehyde |
| Material Status | Commercial: Active |
| Features | Weather resistance is good |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.54 to 1.58 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 190℃，2.16 kg | 1.00 to 5.00 | cm³/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 8000 | MPa | ISO 527-2 |
| tensile strength | |||
| fracture | 1.50 | MPa | |
| — | 60.0 | MPa | |
| Bending modulus | 5500 | MPa | ISO 178 |
| bending strength | 90.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotch Impact strength | |||
| 23℃ | 20 | kJ/m² | ISO 179 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 160 | ℃ | ISO 75-2/B |
| 1.8 MPa, unannealed | 150 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | 160 | ℃ | ISO 306 |
| Melting temperature | |||
| DSC | 165 to 170 | ℃ | ISO 3146 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Compared to the leakage tracing index | < 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 3.20 mm | HB | UL 94 | |
| FMVSS flame retardant rating | < 100 | mm/min | DIN 75200 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 100 | °C | |
| Drying time | 4.0 | hr | |
| Processing (melt) temperature | 190 to 210 | °C | |
| Mold temperature | 75 to 100 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |