| The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PSU |
| Material Status | Commercial: Active |
| Features | V-0 |
| Availabilitys | Africa & Middle East ,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.38 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.30 to 0.40 | % | ASTM D955 |
| Water absorption rate | ASTM D570 | ||
| 24hr | 0.20 | % | ASTM D570 |
| saturated | 0.60 | % | ASTM D570 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 6.4mm, injection molding | 69 | J/m | ASTM D256-A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | ASTM D648 | ||
| 0.45 MPa, annealed, 3.2 mm | 185 | ℃ | ASTM D648 |
| 1.8 MPa, annealed, 3.18 mm | 179 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 2.9E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volume resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | V-0 | UL 94 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Rockwell hardness | |||
| M-level | 92 | ASTM D785 | |
| Tensile modulus | 5520 | MPa | ASTM D638 |
| tensile strength | |||
| fracture | 103 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 | % | ASTM D638 |
| Bending modulus | 5520 | MPa | ASTM D790 |
| bending strength | 152 | MPa | ASTM D790 |
| compressive strength | 138 | MPa | ASTM D695 |
| shear strength | 62.7 | MPa | ASTM D732 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 135 | °C | |
| Drying time | 2.0 | hr | |
| Processing (melt) temperature | 338 to 371 | °C | |
| Mold temperature | 93 to 149 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |