| About |
|---|
| 30% Glass Fiber Reinforced PEEK Compound with High Flowability&& |
| Product Description | |
|---|---|
| Supplier | Polyone |
| Generic | PEEK |
| Material Status | Commercial: Active |
| Features | High Heat Resistance,V-0 |
| Availabilitys | Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.48 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 400℃，2.16kg | 6.0 | g/10min | ASTM D1238 |
| Shrinkage rate | |||
| MD | 0.20 to 0.40 | % | ASTM D955 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 12000 | MPa | ASTM D638 |
| tensile strength | |||
| yield | 180 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 3.0 to 4.0 | % | ASTM D638 |
| Bending modulus | 11000 | MPa | ASTM D790 |
| bending strength | 280 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23 ℃, 3.2mm, injection molding | 110 | J/m | ASTM D256-A |
| Notched impact strength of cantilever beam | |||
| 23℃，3.2 mm | 950 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed, 3.2 mm | 325 | ℃ | ASTM D648 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+14 | ohms | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | V-0 | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 150 to 160 | °C | |
| Drying time | 4.0 to 6.0 | hr | |
| Processing (melt) temperature | 360 to 390 | °C | |
| Mold temperature | 170 to 190 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Type I, 0.20 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |