EKOPREN ® 3SH461

About
EKOPREN ® 3SH461是一种经氯化的聚乙烯材料,。 该产品在北美洲或欧洲有供货,加工方式为:挤出。 EKOPREN ® 3SH461的主要特性有: 通过 ROHS 认证 良好的柔韧性 耐化学品 EKOPREN ® 3SH461的典型应用领域为:电线电缆&&

Product Description
GenericCPE
Material StatusCommercial: Active
FeaturesGood flexibility,Grease resistance,Ozone resistance
AvailabilitysNorth America,Europe
Process MethodsExtrusion

Technical Data
PHYSICALNominal valueUnitTest method
Density1.36g/cm³ASTM D792
Mooney viscosity
100℃50MUASTM D1646

MECHANICALNominal valueUnitTest method
Shore hardness
Shaw’s A73 ASTM D2240

elastic bodyNominal valueUnitTest method
tensile strength
fracture18.5MPaDIN 53504-S2
Tensile strain
fracture520%DIN 53504-S2
tear strength13.0kN/mASTM D624

Aging performanceNominal valueUnitTest method
The rate of change in tensile strength in air
38℃,168 hr-20%
49℃,168 hr-20%
The rate of change in ultimate elongation in air
38℃,168 hr-14%
49℃,168 hr-24%
The rate of change in tensile strength
38℃,24 hr,in Oil-20%
49℃,18 hr,in Oil-30%
Change rate of ultimate elongation
38 ℃, 24 hours in oil-15%
49 ℃, 18 hours in oil-25%

THERMALNominal valueUnitTest method
Operating temperature-50 to 90

FLAME CHARACTERISTICSNominal valueUnitTest method
Extreme oxygen index27%ASTM D2863

Supplementary informationNominal valueUnitTest method
cross-linking
138℃1.5hrASTM D2084
Coking time
138℃5.0minASTM D1646

Process Conditions
Squeeze descriptionNominal valueUnitTest method
ExtrusionNominal valueUnitTest method
Barrel temperature70°C
Barrel 1 zone temperature80°C
Barrel 2 zone temperature100°C
Head temperature110°C

Notes
【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.