| About |
|---|
| EL-Lene H1000PC is a black, bimodal technology, high density polyethylene compound classified as a MRS 10.0 material (PE100) providing superior in mechanical properties and processablity. EL-Lene H1000PC also shows excellent resistance to rapid crack propagation and slow crack growth. In addition, It includes a good dispersion of carbon black pigment and anti-oxidant to ensure excellent long term in UV resistance and thermal stability.&& |
| Product Description | |
|---|---|
| Supplier | SCG |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Excellent Processability,Inoxidizability,Good tear strength,Heat Stabilized |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.959 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，5.0kg | 0.25 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F0 | > 10000 | hr | ASTM D1693 |
| Carbon black content | 2.3 | % | ISO 6964 |
| Carbon Black Dispersion | < 3 | ISO 18553 | |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Oxygen sensing time | |||
| 200℃ | > 60 | min | EN 728 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Rapid Crack Propagation | > 1.00 | MPa | ISO 13477 |
| Resistance to Gas Components | > 20.0 | hr | ISO 1167 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 64 | ASTM D2240 | |
| tensile strength | ISO 527-2/100 | ||
| yield | 23.0 | MPa | ISO 527-2/100 |
| fracture | > 30.0 | MPa | ISO 527-2/100 |
| Tensile strain | |||
| fracture | > 600 | % | ISO 527-2/100 |
| Bending modulus | 1000 | MPa | ASTM D790 |
| Slow crack growth in cut pipe materials | |||
| 80℃ | > 500 | hr | ISO 13479 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 1.0 to 2.0 | hr | |
| Melt temperature | 200 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |