| About |
|---|
| EL-Lene H1000PYL is a yellow, bimodal technology, high density polyethylene compound that is specially designed for striping. EL-Lene H1000PYL consists of high UV stabilizer and anti-oxidant which are well dispersed and provides outstanding UVresistance and high thermal stability for long term using.&& |
| Product Description | |
|---|---|
| Supplier | SCG |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Excellent Processability,Inoxidizability,Heat Stabilized |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.951 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，5.0kg | 0.28 | g/10min | ISO 1133 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| F0 | > 10000 | hr | ASTM D1693 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | ASTM D256 | ||
| -20℃ | 200 | J/m | ASTM D256 |
| 0℃ | 260 | J/m | ASTM D256 |
| 23℃ | 300 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -60.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 122 | ℃ | ASTM D1525 |
| Oxygen sensing time | |||
| 200℃ | > 50 | min | ISO 10837 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 66 | ASTM D2240 | |
| tensile strength | ISO 527-2/100 | ||
| yield | 23.0 | MPa | ISO 527-2/100 |
| fracture | 36.0 | MPa | ISO 527-2/100 |
| Tensile strain | |||
| fracture | 850 | % | ISO 527-2/100 |
| Bending modulus | 1000 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 200 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |