| About |
|---|
| EL-LENE H5604F is a product of bi-modal process from Mitsui Chemicals, Inc. of Japan.&& |
| Product Description | |
|---|---|
| Supplier | SCG |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,High impact resistance,Low speed solidification point,Food contact compliance,Moisture resistance |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.956 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.040 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 25% non-ionic surfactant, molded, F50 | > 1000 | hr | ASTM D1693B |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | 10 to 25 µ | ||
| Secant modulus | ASTM D882 | ||
| 2% secant, MD: 12 µ m | 804 | MPa | |
| 2% secant, TD: 12 µ m | 785 | MPa | |
| tensile strength | ASTM D882 | ||
| TD, yield, 12 µ m | 24.5 | MPa | |
| MD, fracture, 12 µ m | 60.8 | MPa | |
| TD, fracture, 12 µ m | 30.4 | MPa | |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 12 µ m | 240 | % | |
| TD, fracture, 12 µ m | 450 | % | |
| Drop hammer impact | |||
| 12 µm | 140 | g | ASTM D1709 |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：12 µm | 3.0 | g | |
| TD：12 µm | 80 | g |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -60.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 124 | ℃ | ASTM D1525 |
| Melting temperature | 131 | ℃ | ASTM D2117 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |