| About |
|---|
| EL-Lene H6007JU is a high density polyethylene resin with good processibility and UV resistance suitable for industrial product produced from injection molding process.&& |
| Product Description | |
|---|---|
| Supplier | SCG |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Weather resistance is good,Excellent Processability,High impact resistance,Food contact compliance |
| Availabilitys | North America,Asia Pacific |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.964 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 7.5 | g/10min | ASTM D1238 |
| Shrinkage rate | ASTM D955 | ||
| MD：2.0 mm | 1.6 | % | ASTM D955 |
| TD：2.0 mm | 0.96 | % | ASTM D955 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 25% non-ionic surfactant, molded, F50 | 4.00 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 34 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 75.0 | ℃ | ASTM D648 |
| Embrittlement temperature | -60.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 127 | ℃ | ASTM D1525 |
| Melting temperature | 133 | ℃ | ASTM D2117 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 68 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| yield | 30.4 | MPa | ASTM D638 |
| fracture | 21.6 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | > 650 | % | ASTM D638 |
| Bending modulus | 1320 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 200 to 250 | °C | |
| Mold temperature | 20 to 60 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |