| About |
|---|
| EL-Lene H6670B is a high density polyethylene resin suitable for producing milk bottles by using Extrusion blow molding machine.&& |
| Product Description | |
|---|---|
| Supplier | SCG |
| Generic | HDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Good liquidity,Good Printability,Food contact compliance,Low odor |
| Availabilitys | North America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.966 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.70 | g/10min | ASTM D1238 |
| ESCR(Environmental Stress Cracking Resistance) | |||
| 50 ℃, 25% non-ionic surfactant, molded, F50 | 24.0 | hr | ASTM D1693B |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 150 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Embrittlement temperature | < -60.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 128 | ℃ | ASTM D1525 |
| Melting temperature | 132 | ℃ | ASTM D2117 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 68 | ASTM D2240 | |
| tensile strength | ASTM D638 | ||
| yield | 31.4 | MPa | ASTM D638 |
| fracture | 32.4 | MPa | ASTM D638 |
| Tensile strain | |||
| fracture | 1200 | % | ASTM D638 |
| Bending modulus | 1470 | MPa | ASTM D790 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 170 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2.0 in/min |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |