| About |
|---|
| EL-PRO P600F is a Homopolymer polypropylene resin without slip and antiblock agent.&& |
| Product Description | |
|---|---|
| Supplier | SCG |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good flexibility,Hydrolysis stability,Good wear resistance,Grease resistance,Solvent resistance,Fuel resistance |
| Availabilitys | North America |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 10 | g/10min | ASTM D1238 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Bending modulus | 1670 | MPa | ASTM D790 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Secant modulus | ASTM D882 | ||
| 2% secant, MD: 25 µ m | 686 | MPa | ASTM D882 |
| 2% secant, TD: 25 µ m | 539 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 25 µ m | 28.4 | MPa | ASTM D882 |
| TD, yield, 25 µ m | 19.6 | MPa | ASTM D882 |
| MD, fracture, 25 µ m | 27.5 | MPa | ASTM D882 |
| TD, fracture, 25 µ m | 25.5 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 25 µ m | 850 | % | ASTM D882 |
| TD, fracture, 25 µ m | 770 | % | ASTM D882 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 25 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 110 | ℃ | ASTM D648 |
| Embrittlement temperature | < -10.0 | ℃ | ASTM D746 |
| Vicat Softening Temp | 155 | ℃ | ASTM D1525 |
| Melting temperature | 160 | ℃ | ASTM D2117 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | 75 | ASTM D2457 | |
| Haze | 8.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |