| About |
|---|
| Low density I-skin foam system (natural color) HFC 245fa-blown, two-component microcellular polyurethane foam system designed for molding of miscellaneous Integral Skin articles that require good skin at relatively low molded densities. Depending on the application requirements and the processing conditions this system can provide Exceptional skin formation when casted in metal tools at low mold temperatures Wide range of molded densities from 10 to 25 pcf Hardness range from 10 to 70 Shore A Wide processing window on both low-pressure and high-pressure equipment&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | PUR |
| Material Status | Commercial: Active |
| Features | Excellent Processability,Low density |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| — | 0.256 | g/cm³ | |
| — | 0.320 | g/cm³ | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s A | 45 | ||
| Shaw’s A | 55 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 1.17 | MPa | |
| yield | 1.86 | MPa | |
| Tensile strain | |||
| fracture | 130 | % | ASTM D412 |
| tear strength | |||
| — | 4.03 | kN/m | |
| — | 5.78 | kN/m | |
| cracking | 1.6 | kN/m | |
| cracking | 2.1 | kN/m | |
| Compression deformation | |||
| 70℃，22 hr | 15 | % | |
| 70℃，22 hr | 10 | % |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Burning rate | |||
| — | 0.0 | mm/min | |
| — | 0.0 | mm/min |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Hand Mix |
| 3. High Pressure |
| 4. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |