| About |
|---|
| Halogen-free flame retardant, thermoplastic Polyether-Polyurethane with outstanding hydrolysis resistance, low temperature flexibility and high resistance to micro-organisms.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | TPU-醚 |
| Material Status | Commercial: Active |
| Features | Hydrolysis stability,Antimicrobial properties,Halogen free,Flame Characteristics,Low temperature toughness |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.25 | g/cm³ | ISO 1183/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 3 seconds | 90 | ISO 7619 | |
| Wear amount | 30.0 | mm³ | ISO 4649-A |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | DIN 53504-S2 | ||
| 300% strain | 11.0 | MPa | DIN 53504-S2 |
| 20% strain | 5.00 | MPa | DIN 53504-S2 |
| 100% strain | 8.00 | MPa | DIN 53504-S2 |
| yield | 15.0 | MPa | DIN 53504-S2 |
| yield | 25.0 | MPa | DIN 53504-S2 |
| Tensile strain | DIN 53504-S2 | ||
| fracture | 640 | % | DIN 53504-S2 |
| fracture | 550 | % | DIN 53504-S2 |
| tear strength | 60 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 23℃，72 hr | 26 | % | ISO 815 |
| 70℃，24 hr | 43 | % | ISO 815 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30℃ | 46 | kJ/m² | ISO 179 |
| 23℃ | No Break | ISO 179 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Drying temperature | 90 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 40 | °C | |
| Barrel rear temperature | 205 to 215 | °C | |
| Barrel middle temperature | 210 to 225 | °C | |
| Barrel front temperature | 215 to 225 | °C | |
| Nozzle temperature | 220 to 230 | °C | |
| Processing (melt) temperature | 215 to 225 | °C | |
| Mold temperature | 20 to 40 | °C | |
| Injection speed | Slow | ||
| Back pressure | 5.00 to 15.0 | MPa | |
| Drying temperature | 90 to 110 | °C | |
| Drying time | 3.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Barrel 1 zone temperature | 160 to 180 | °C | |
| Barrel 2 zone temperature | 180 to 200 | °C | |
| Barrel 3 zone temperature | 190 to 210 | °C | |
| Barrel 4 zone temperature | 200 to 220 | °C | |
| Connector temperature | 200 to 220 | °C | |
| Nozzle temperature | 190 to 210 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. after storage in water at 80°C for 42 days |
| 3. Method Bb, Angle (Nicked) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |