| Thermoplastic Polyester-Polyurethane with excellent mechanical properties and a high abrasion resistance.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Good wear resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.22 | g/cm³ | ISO 1183/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 3 seconds | 60 | DIN 7619-1 | |
| Wear amount | 90.0 | mm³ | ISO 4649-A |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 24.0 | MPa | DIN 53504-S2 |
| 300% strain | 6.00 | MPa | DIN 53504-S2 |
| 20% strain | 1.00 | MPa | DIN 53504-S2 |
| 100% strain | 2.50 | MPa | DIN 53504-S2 |
| Tensile strain | |||
| fracture | 850 | % | DIN 53504-S2 |
| tear strength | 50 | kN/m | ISO 34-1 |
| Compression deformation | ISO 815 | ||
| 23℃，72 hr | 29 | % | ISO 815 |
| 70℃，24 hr | 45 | % | ISO 815 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 80 to 90 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Recommended maximum moisture content | 0.020 | % | |
| Hopper temperature | 40 | °C | |
| Barrel rear temperature | 195 to 205 | °C | |
| Barrel middle temperature | 200 to 210 | °C | |
| Barrel front temperature | 200 to 210 | °C | |
| Nozzle temperature | 205 to 215 | °C | |
| Processing (melt) temperature | 200 to 210 | °C | |
| Mold temperature | 20 to 40 | °C | |
| Injection speed | Slow | ||
| Back pressure | 5.00 to 15.0 | MPa | |
| Screw length to diameter ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw compression ratio | 2.0:1.0 to 3.0:1.0 | ||
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method Bb, Angle (Nicked) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |