| About |
|---|
| Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties, outstanding wear resistance, good tensile strength, good damping and resilience performance and superior low temperature flexibility. Typical applications Sport-shoe soles and accessories, Skiboot shells, technical mouldings, e.g. seals, castor tyres, tubing. Certain UV stabilised B grades are available on request&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,Elastic,Low temperature toughness,Good wear resistance |
| Availabilitys | Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.17 | g/cm³ | ISO 1183 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 5.0E+7 | Ω.cm | IEC 60093 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | – | HB | UL-94 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| 23℃ | NB | kJ/m² | ISO 179/1eA |
| -30℃ | NB | kJ/m² | ISO 179/1eA |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 3 seconds | 63 | ISO 868 | |
| tensile strength | |||
| ℃ | 30 | MPa | ISO 527-2 |
| Tensile strain | |||
| Fracture, 23 ℃ | 800 | % | ISO 527-2 |
| tear strength | |||
| MD | 50 | KN/m | ISO 34-1 |
| Compression deformation | |||
| 70℃，24 hr | 30 | % | ISO 815 |
| 23℃，72 hr | 20 | % | ISO 815 |
| Wear amount | 60 | mm³ | ISO 4649-A |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion molding conditions | Nominal value | Unit | Test method |
| Drying temperature | 60-90 | °C | |
| Drying time | 3.0-8.0 | Hr | |
| Recommended moisture content | <=0.20 | % | |
| Barrel rear temperature | 150-190 | °C | |
| Barrel middle temperature | 160-200 | °C | |
| Barrel front temperature | 170-210 | °C | |
| Nozzle temperature | 180-220 | °C | |
| Mold temperature | 10-80 | °C | |
| Drying temperature | 60-90 | °C | |
| Drying time | 3.0-8.0 | Hr | |
| Recommended moisture content | <=0.20 | % | |
| First zone temperature | 130-170 | °C | |
| Zone 2 temperature | 140-180 | °C | |
| Third zone temperature | 150-190 | °C | |
| Fourth zone temperature | 160-200 | °C | |
| Fifth zone temperature | 170-210 | °C | |
| Die temperature | 180-220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. after storage in water for 21 days at 80°C |
| 3. Method Bb, Angle (Nicked) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |