| About |
|---|
| Elastollan® C59D exhibits excellent abrasion resistance and toughness, good hydrolytic stability, good heat, oil, fuel and solvent resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® C59D is rated UL-94 V-2 in vertical flame test for wall thickness of 0.75 mm. Elastollan® C59D is supplied uncolored in diced form.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Good flexibility,Hydrolysis stability,High Heat Resistance,Good tear strength,Good wear resistance,Solvent resistance,V-2 |
| Availabilitys | North America |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.23 | g/cm³ | ASTM D792 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shaw’s D | 56 | ASTM D2240 | |
| Tensile modulus | |||
| injection molding | 131 | MPa | ASTM D412 |
| Bending modulus | |||
| injection molding | 138 | MPa | ASTM D790 |
| Taber abraser | 45.0 | mg | ASTM D1044 |
| Abrasion（DIN） | 25 | mm³ | DIN 53516 |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | 50.3 | MPa | ASTM D412 |
| 300% strain | 46.2 | MPa | ASTM D412 |
| 100% strain | 23.4 | MPa | ASTM D412 |
| Tensile strain | |||
| fracture | 430 | % | ASTM D412 |
| tear strength | 210 | kN/m | ASTM D624 |
| Compression deformation | ASTM D395B | ||
| 23℃，22 hr | 30 | % | ASTM D395B |
| 70℃，22 hr | 50 | % | ASTM D395B |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Glass transition temperature | -15.0 | ℃ | Internal Method |
| Vicat Softening Temp | 143 | ℃ | ASTM D1525 |
| Softening temperature | |||
| DMA | 131 | ℃ | Internal Method |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame retardant level | |||
| 0.75 mm | V-2 | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 110 to 120 | °C | |
| Drying time | 2.0 to 3.0 | hr | |
| Recommended maximum moisture content | 0.030 | % | |
| Barrel rear temperature | 210 to 230 | °C | |
| Barrel middle temperature | 210 to 230 | °C | |
| Barrel front temperature | 210 to 230 | °C | |
| Nozzle temperature | 220 to 240 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Die C |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |