| About |
|---|
| Highly transparent, aliphatic, light-resistant, thermoplastic Polyester-Polyurethane.&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Aliphatic series |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.12 | g/cm³ | ISO 1183/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 3 seconds | 86 | ISO 7619 | |
| Wear amount | 245 | mm³ | ISO 4649-A |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 28.0 | MPa | DIN 53504-S2 |
| 300% strain | 10.0 | MPa | DIN 53504-S2 |
| 20% strain | 1.80 | MPa | DIN 53504-S2 |
| 100% strain | 4.00 | MPa | DIN 53504-S2 |
| Tensile strain | |||
| fracture | 500 | % | DIN 53504-S2 |
| tear strength | 65 | kN/m | ISO 34-1 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Barrel 1 zone temperature | 140 to 160 | °C | |
| Barrel 2 zone temperature | 145 to 165 | °C | |
| Barrel 3 zone temperature | 150 to 170 | °C | |
| Barrel 4 zone temperature | 155 to 175 | °C | |
| Connector temperature | 160 to 180 | °C | |
| Melt temperature | 180 to 230 | °C | |
| Nozzle temperature | 160 to 180 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method Bb, Angle (Nicked) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |