Elastollan® N 1195 A 10 U

About
Bio based thermoplastic Polyether-Polyurethane Elastomer with outstanding hydrolysis resistance, low temperature flexibility and resistance to micro-organisms. Processable by injection moulding and extrusion.

Product Description
Supplier	BASF
Material Status	Commercial: Active
Features	Biocompatible,Hydrolysis stability,Good flexibility

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.14	g/cm³	ISO 1183

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
A	95	Shore A	ISO 7619-1
D	52	Shore D	ISO 7619-1
Tensile Strength	55	MPa	DIN 53504-S2
Elongation at Break	450	%	DIN 53504-S2
tear strength	120	N/mm	ISO 34-1
Abrasion Loss	40	mm³	ISO 4649
Biobased content	45	%

Process Conditions
Injection Molding	Nominal value	Unit	Test method
Drying time	2-3	h
Drying temperature	90-110	℃
Screw speed	< 0.2	m/s
Melt pressure	400-600	Bar
Injection speed	低速
Retention time of melt	<10	min
Feed Temperature	40	℃
Barrel – Zone 1 Temperature	210-220	℃
Barrel – Zone 2 Temperature	215-225	℃
Barrel – Zone 3 Temperature	220-230	℃
Barrel – Zone 4 Temperature	220-230	℃
Nozzle Temperature	225-235	℃
Melt Temperature	220-230	℃
Mold Temperature	30-60	℃

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.