| About |
|---|
| Thermoplastic Polyether and Polyester Polyurethane Special products with excellent mechanical properties, outstanding wear resistance, good damping and resilience performance and excellent tear strength. Typical applications Application specific formulations. Suitable for foaming&& |
| Product Description | |
|---|---|
| Supplier | BASF |
| Generic | TPU-酯 |
| Material Status | Commercial: Active |
| Features | Elastic,Good tear strength,Good wear resistance |
| Availabilitys | Europe |
| Process Methods | Extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.18 | g/cm³ | ISO 1183/A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Shore hardness | |||
| Shore A, 3 seconds | 40 | ISO 7619 | |
| Wear amount | 165 | mm³ | ISO 4649-A |
| elastic body | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 12.0 | MPa | DIN 53504 |
| 300% strain | 2.50 | MPa | DIN 53504 |
| 20% strain | 0.500 | MPa | DIN 53504 |
| 100% strain | 1.00 | MPa | DIN 53504 |
| Tensile strain | |||
| fracture | 1200 | % | DIN 53504 |
| tear strength | 27 | kN/m | ISO 34-1 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Processing (melt) temperature | 175 to 240 | °C | |
| Mold temperature | 20 to 70 | °C | |
| Melt temperature | 175 to 220 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method Bb, Angle (Nicked) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |