| Electrafil® PA6/6 CF40 BK is a Polyamide 66 (Nylon 66) product filled with 40% carbon fiber. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Electrafil® PA6/6 CF40 BK include automotive, business/office goods, conveyors, engineering/industrial parts and packaging. Characteristics include: Flame Rated RoHS Compliant Conductive&& |
| Product Description | |
|---|---|
| Generic | PA66 |
| Material Status | Commercial: Active |
| Features | Conductive,Antistatic property,HB |
| Availabilitys | Africa & Middle East ,North America,Latin America,Asia Pacific,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.33 | g/cm³ | ASTM D792 |
| Shrinkage rate | |||
| MD | 0.10 | % | ASTM D955 |
| Water absorption rate | |||
| 24hr | 0.60 | % | ASTM D570 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 23℃ | 28300 | MPa | ASTM D638 |
| tensile strength | |||
| 23℃ | 276 | MPa | ASTM D638 |
| Tensile strain | |||
| Fracture, 23 ℃ | 1.8 | % | ASTM D638 |
| Bending modulus | |||
| 23℃ | 23400 | MPa | ASTM D790 |
| bending strength | |||
| 23℃ | 407 | MPa | ASTM D790 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃，3.2mm | 96 | J/m | ASTM D256 |
| Notched impact strength of cantilever beam | |||
| 23℃，3.2 mm | 800 | J/m | ASTM D256 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 1.8 MPa, unannealed | 257 | ℃ | ASTM D648 |
| 0.45 MPa, unannealed | 263 | ℃ | ASTM D648 |
| Linear coefficient of thermal expansion | |||
| MD | 1.4E-5 | 1/℃ | ASTM D696 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 55 | ohms | ASTM D257 |
| Volume resistivity | 5.5 | ohms·cm | ASTM D257 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Drying temperature | 82 | °C | |
| Drying time | 2.0 to 4.0 | hr | |
| Recommended maximum moisture content | 0.10 | % | |
| Barrel rear temperature | 277 to 288 | °C | |
| Barrel middle temperature | 288 to 299 | °C | |
| Barrel front temperature | 282 to 293 | °C | |
| Nozzle temperature | 282 to 288 | °C | |
| Processing (melt) temperature | 282 to 304 | °C | |
| Mold temperature | 79 to 104 | °C | |
| Injection speed | Slow-Moderate | ||
| Back pressure | 0.00 to 0.345 | MPa | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |