Electroblend® PBT-1901

About
Electroblend® PBT-1901 is a glass fiber reinforced antistatic polybutylene terephthalate compound characterized by high mechanical with lower shrinkage properties.&&

Product Description
Generic	polybutylene terephthalate
Material Status	Commercial: Active
Features	Low contractility,Antistatic property,HB
Availabilitys	Asia Pacific
Process Methods	Injection Molding

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	1.51	g/cm³	ASTM D792
Shrinkage rate
MD：3.2 mm	0.20 to 0.60	%	ASTM D955

MECHANICAL	Nominal value	Unit	Test method
tensile strength	85.0	MPa	ASTM D638
Tensile strain
fracture	2.5	%	ASTM D638
Bending modulus	7200	MPa	ASTM D790
bending strength	110	MPa	ASTM D790

IMPACT	Nominal value	Unit	Test method
Impact strength of cantilever beam notch
23℃	75	J/m	ASTM D256

Electrical performance	Nominal value	Unit	Test method
Surface resistivity	1.0E+6 to 1.0E+8	ohms	ASTM D257

FLAME CHARACTERISTICS	Nominal value	Unit	Test method
1.60 mm	HB		UL 94

Process Conditions
injection	Nominal value	Unit	Test method
Drying temperature	120	°C
Drying time	4.0 to 6.0	hr
Barrel rear temperature	240 to 245	°C
Barrel middle temperature	245 to 250	°C
Barrel front temperature	250 to 255	°C
Nozzle temperature	255 to 260	°C
Processing (melt) temperature	240 to 260	°C
Mold temperature	80.0 to 100	°C

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.