ELITE™ 5100G

About
For industrial and consumer film applications Extremely high impact strength Low blocking tendencies for improved handling and convertibility Complies with: U.S. FDA 21 CFR 177.1520 (c) 3.2a. Canadian HPFB No Objection Consult the regulations for complete details. ELITE™ 5100G Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow Plastics. It offers excellent impact strength, good tensile and puncture properties for thick and thin gauge industrial and consumer blown film applications. This resin exhibits higher hot tack strengths than LLDPE, making it ideal for automated packaging applications.&&

About

For industrial and consumer film applications Extremely high impact strength Low blocking tendencies for improved handling and convertibility Complies with: U.S. FDA 21 CFR 177.1520 (c) 3.2a. Canadian HPFB No Objection Consult the regulations for complete details. ELITE™ 5100G Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow Plastics. It offers excellent impact strength, good tensile and puncture properties for thick and thin gauge industrial and consumer blown film applications. This resin exhibits higher hot tack strengths than LLDPE, making it ideal for automated packaging applications.&&

Product Description
Supplier	DOW
Generic	EPE
Material Status	Commercial: Active
Availabilitys	North America,Latin America,Asia Pacific,Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.920	g/cm³	ASTM D792
Melt Flow Rate
190℃，2.16kg	0.85	g/10min	ASTM D1238

film	Nominal value	Unit	Test method
film thickness
test	25	µm
Membrane puncture strength	5.76	J	Internal Method
Membrane puncture force	64.5	N	Internal Method
Membrane puncture resistance	28.3	J/cm³	Internal Method
Membrane strength			ASTM D882
MD	98.5	J/cm³	ASTM D882
TD	98.5	J/cm³	ASTM D882
Secant modulus			ASTM D882
1% secant, MD	272	MPa	ASTM D882
2% secant, MD	231	MPa	ASTM D882
1% secant, TD	309	MPa	ASTM D882
2% secant, TD	256	MPa	ASTM D882
tensile strength			ASTM D882
MD, yield	11.9	MPa	ASTM D882
TD, yield	12.4	MPa	ASTM D882
MD, fracture	43.6	MPa	ASTM D882
TD, fracture	36.0	MPa	ASTM D882
Tensile strain			ASTM D882
MD, fracture	480	%	ASTM D882
TD, fracture	620	%	ASTM D882
Drop hammer impact	540	g	ASTM D1709-A
Elmandorf tear strength			ASTM D1922
MD	260	g	ASTM D1922
TD	670	g	ASTM D1922

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	106	℃	ASTM D1525
Melting temperature
DSC	123	℃	Internal Method

optical performance	Nominal value	Unit	Test method
gloss
45°	33		ASTM D2457
Haze	20	%	ASTM D1003

Notes
1. Typical properties: these are not to be construed as specifications.
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

1. Typical properties: these are not to be construed as specifications.

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.