| About |
|---|
| ELITE™ 5230S Enhanced Polyethylene Resin is produced via INSITE™ Technology from Dow. This resin offers high impact strength and good puncture resistance at moderate stretch levels for irregularly shaped loads. In addition, this resin provides excellent extensibility for higher yields on regular loads. Excellent extensibility High impact and puncture resistance Complies with: U.S. FDA FCN 424 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EPE |
| Material Status | Commercial: Active |
| Availabilitys | North America |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.916 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 4.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 20 | µm | |
| Membrane puncture force | |||
| 20 µm | 48.9 | N | Internal Method |
| Membrane puncture resistance | |||
| 20 µm | 27.0 | J/cm³ | Internal Method |
| tensile strength | |||
| MD, yield, 20 µ m | 9.07 | MPa | |
| TD, yield, 20 µ m | 8.39 | MPa | |
| MD, fracture, 20 µ m | 46.0 | MPa | |
| TD, fracture, 20 µ m | 38.1 | MPa | |
| Tensile strain | |||
| MD, fracture, 20 µ m | 540 | % | |
| TD, fracture, 20 µ m | 720 | % | |
| Drop hammer impact | |||
| 20 µm | 320 | g | ASTM D1709-B |
| Elmandorf tear strength | |||
| MD：20 µm | 310 | g | |
| TD：20 µm | 510 | g | |
| Final stretching | |||
| 20.3 µm | 330 | % | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | |||
| DSC | 122 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45°，20.3 µm | 95 | ASTM D2457 | |
| Haze | |||
| 20.3 µm | 0.50 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Squeeze description | Nominal value | Unit | Test method |
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 271 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 250% pre-stretch; On-Pallet testing. |
| 3. On-Pallet testing |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |