| ELITE™ 5400GS Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow. It offers extremely high impact resistance, combined with excellent tear, tensile and optical properties for high strength blown film applications. In addition, ELITE 5400GS Enhanced Polyethylene Resin offers a unique combination of low seal initiation, higher modulus, and low blocking tendencies for automated packaging applications. Applications: For food and specially packaging films. Extremely high impact resistance. Excellent tear, tensile, and optical properties. Low seal initiation temperatures and high hot tack strengths for form-fill-seal applications. Complies with: EU, No 10/2011 U.S. FDA FCN 424 Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EPE |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.916 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.0 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 51 | µm | |
| Membrane puncture strength | |||
| 51 µm | 5.50 | J | Internal Method |
| Membrane puncture force | |||
| 51 µm | 107 | N | Internal Method |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD: 51 µ m | 171 | MPa | ASTM D882 |
| 1% secant, TD: 51 µ m | 194 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield, 51 µ m | 11.3 | MPa | ASTM D882 |
| TD, yield, 51 µ m | 11.2 | MPa | ASTM D882 |
| MD, fracture, 51 µ m | 54.0 | MPa | ASTM D882 |
| TD, fracture, 51 µ m | 52.0 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture, 51 µ m | 640 | % | ASTM D882 |
| TD, fracture, 51 µ m | 660 | % | ASTM D882 |
| Drop hammer impact | |||
| 51 µm | > 850 | g | ASTM D1709-B |
| Elmandorf tear strength | ASTM D1922 | ||
| MD：51 µm | 630 | g | ASTM D1922 |
| TD：51 µm | 770 | g | ASTM D1922 |
| Initial sealing temperature | |||
| 51 µm | 90.0 | ℃ | Internal Method |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 122 | ℃ | DSC |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 20°，51 µm | 77 | ASTM D2457 | |
| Haze | |||
| 51 µm | 9.5 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 246 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Blown film extruded at 232-246°C, 2.5:1 BUR, 1.9 mm die gap. |
| 3. Type A; Blown film extruded at 232-246°C, 2.5:1 BUR, 1.9 mm die gap. |
| 4. Blown film extruded at 232-246°C, 2.5:1 BUR, 1.9 mm die gap. Temperature at which 5.25 N/15 mm heat seal strength is achieved. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |