| About |
|---|
| ELITE™ 5800G is an Enhanced Polyethylene Resin for Extrusion. Main Characteristics: High performance sealant Designed for use on typical extrusion coating hardware Robust extrusion and melt drawing performance for high capacity operations Complies with: U.S. FDA, Unspecified Rating EU, No 10/2011 Canadian HPFB No Objection Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EPE |
| Material Status | Commercial: Active |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.911 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 12 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| 2% secant | 134 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| yield | 7.10 | MPa | ISO 527-3 |
| fracture | 18.1 | MPa | ISO 527-3 |
| Tensile strain | |||
| fracture | 690 | % | ISO 527-3 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 86.0 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 103 | ℃ | Internal Method |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 270 to 320 | °C | |
| Shrinkage 2 (290癈) | 159.0 | mm | |
| Drop down 3 | 350 | m/min | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Acceleration from 15g/m² at 100mpm. |
| 3. 25g/m² at 100mpm. |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |