ELITE™ 5940G

About
ELITE™ 5940G Enhanced Polyethylene Resin is a copolymer produced via INSITE™ Technology from Dow. Main Characteristics: MDPE with excellent balance of stiffness and toughness. Excellent processability. Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a Canadian HPFB No Objection Consult the regulations for complete details&&

film	Nominal value	Unit	Test method
film thickness
test	25	µm
Membrane puncture strength	1.92	J
Membrane puncture force	44.5	N
Membrane puncture resistance	9.51	J/cm³	Internal Method
Membrane strength			ASTM D882
MD	108	J/cm³	ASTM D882
TD	124	J/cm³	ASTM D882
Secant modulus			ASTM D882
1% secant, MD	625	MPa	ASTM D882
2% secant, MD	503	MPa	ASTM D882
1% secant, TD	758	MPa	ASTM D882
2% secant, TD	607	MPa	ASTM D882
tensile strength			ASTM D882
MD, yield	20.7	MPa	ASTM D882
TD, yield	24.1	MPa	ASTM D882
MD, fracture	35.9	MPa	ASTM D882
TD, fracture	32.4	MPa	ASTM D882
Tensile strain			ASTM D882
MD, fracture	460	%	ASTM D882
TD, fracture	640	%	ASTM D882
Drop hammer impact	120	g	ASTM D1709-A
Elmandorf tear strength			ASTM D1922
MD	40	g	ASTM D1922
TD	650	g	ASTM D1922

THERMAL	Nominal value	Unit	Test method
Vicat Softening Temp	122	℃	ASTM D1525
Melting temperature
DSC	126	℃	Internal Method

optical performance	Nominal value	Unit	Test method
gloss
45°	20		ASTM D2457
Haze	30	%	ASTM D1003

Notes
1. Typical properties: these are not to be construed as specifications.
2. Method B
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.