| Main Characteristics: HDPE with excellent moisture barrier Processes with low back pressure and excellent bubble stability Complies with: U.S. FDA 21 CFR 177.1520 (c) 2.2 EU, No 10/2011 Canadian HPFB No Objection Consult the regulations for complete details.&& |
| Product Description | |
|---|---|
| Supplier | DOW |
| Generic | EPE |
| Material Status | Commercial: Active |
| Availabilitys | North America,Latin America,Asia Pacific |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.962 | g/cm³ | ASTM D792 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 0.85 | g/10min | ASTM D1238 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Membrane puncture strength | 0.339 | J | |
| Membrane puncture force | 13.3 | N | |
| Membrane puncture resistance | 1.41 | J/cm³ | Internal Method |
| Membrane strength | ASTM D882 | ||
| MD | 141 | J/cm³ | ASTM D882 |
| TD | 128 | J/cm³ | ASTM D882 |
| Secant modulus | ASTM D882 | ||
| 1% secant, MD | 1120 | MPa | ASTM D882 |
| 2% secant, MD | 876 | MPa | ASTM D882 |
| 1% secant, TD | 1330 | MPa | ASTM D882 |
| 2% secant, TD | 1020 | MPa | ASTM D882 |
| tensile strength | ASTM D882 | ||
| MD, yield | 28.3 | MPa | ASTM D882 |
| TD, yield | 30.3 | MPa | ASTM D882 |
| MD, fracture | 37.2 | MPa | ASTM D882 |
| TD, fracture | 24.1 | MPa | ASTM D882 |
| Tensile strain | ASTM D882 | ||
| MD, fracture | 500 | % | ASTM D882 |
| TD, fracture | 600 | % | ASTM D882 |
| Drop hammer impact | 40 | g | ASTM D1709-A |
| Elmandorf tear strength | ASTM D1922 | ||
| MD | 13 | g | ASTM D1922 |
| TD | 400 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temp | 130 | ℃ | ASTM D1525 |
| Melting temperature | |||
| DSC | 134 | ℃ | Internal Method |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45° | 14 | ASTM D2457 | |
| Haze | 42 | % | ASTM D1003 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Method B |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |