| About |
|---|
| High heat resistance ABS ISO shortname: ISO 2580-1 ABS 1-M, MG, 105-15-16-20 Major Benefits: Excellent balance of impact strength and flowability Super low emission grade Lower mould deposits in injection molding processing applications Better dimensional under heat Chemical Composition: Acrylonitrile-butadiene-styrene (ABS) copolymer modified with poly(styrene-co-maleimide) (SMI)&& |
| Product Description | |
|---|---|
| Material Status | Commercial: Active |
| Features | High Heat Resistance,HB,Low odor |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume Rate | |||
| 220℃，10kg | 16 | cm³/10min | ISO 1133 |
| Molding shrinkage | |||
| Parallel | 0.6-0.7 | % | ISO 294-4 |
| Normal | 0.6-0.7 | % | ISO 294-4 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile Strength | |||
| Yield yld | 42 | MPa | ISO 527-2 |
| Elongation at Break | 32 | % | ISO 527-1,2 |
| Tensile Modulus | 2150 | MPa | ISO 527 |
| Flexural Modulus | 2260 | MPa | ISO 178 |
| Flexural Strength | 66 | MPa | ISO 178 |
| Ball indentation hardness | 95 | N/mm² | ISO 2039-1 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Izod Notched Impact strength | |||
| 23℃ | 18 | KJ/m² | ISO 180/1A |
| -30℃ | 11 | KJ/m² | ISO 180/1A |
| Charpy Notched Impact Strength | 19 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| B50, 50ºC/h | 103 | ℃ | ISO 306/B |
| B120, 120ºC/h | 105 | ℃ | ISO 306/B |
| Hot deformation temperature HDT | |||
| 1.80 MPa | 99 | ℃ | ISO 75-1/-2 |
| 0.45 MPa | 104 | ℃ | ISO 75-1/-2 |
| Coeff. of linear thermal expansion | |||
| Parallel | 0.99 | ×10-4/℃ | ISO 11359-2 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Flame Class Rating | |||
| 1.6 mm | HB | calss | UL 94 |
| FMVSS flame retardant rating | |||
| 200x105x2mm | <50 | mm/min | ISO 3795 |
| Process Conditions | |||
|---|---|---|---|
| Injection Molding | Nominal value | Unit | Test method |
| Melt Temperature | 240 | ℃ | |
| Mold Temperature | 70 | ℃ | |
| Injection velocity | 240 | mm/s | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2 mm |
| 3. 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Rate A (50°C/h), Loading 2 (50 N) |
| 7. US-FMVSS |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |