| About |
|---|
| ELIX ABS M203FC Injection Moulding grade for medical applications (e.g. inhalers, roller clamps, spikes, etc.)/ Biocompatible with up to 30 days human contact duration according to USP Class VI and ISO 10993-1. Food contact acc. to BfR and FDA, DMF registered. Easy flowing, high gloss, standard impact strength. ISO Shortname: ISO 2580-ABS 0,MG,095-25-16-25&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good surface appearance,High impact resistance,Good liquidity,Biocompatible,Food contact compliance |
| Availabilitys | North America,Europe |
| Process Methods | Injection Molding |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 1.05 | g/cm³ | ISO 1183 |
| Shrinkage rate | 0.4-0.7 | % | ISO 294-4 |
| Melt Flow Rate | |||
| 220℃，10.0kg | 31 | g/10min | ISO 1133 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 98 | ℃ | ISO 75-2/Bf |
| 1.8 MPa, annealed | 94 | ℃ | ISO 75-2/Af |
| Vicat Softening Temp | |||
| B50 | 99 | ℃ | ISO 306/A50 |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Volumetric resistance | 1.0E+13 | Ω.cm | IEC 60093 |
| Surface resistance | 1.0E+15 | Ω.cm | IEC 60093 |
| Insulation strength | |||
| 1.00mm | 35 | KV/mm | IEC 60243-1 |
| Dielectric constant | |||
| 2.9 | 1 MHz | IEC 60250 | |
| 3 | 100 Hz | IEC 60250 | |
| Dissipation factor | |||
| 0.05 | IEC 60250 | ||
| 0.09 | IEC 60250 | ||
| Compared to the leakage tracing index | 600 | V | IEC 60112 |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| Igniting temperature of the hot wire | |||
| 2 mm | 700 | ℃ | IEC 60695-2-12 |
| Other performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting temperature | 240 | ℃ | ISO 294 |
| Injection speed | 240 | mm/sec | ISO 294 |
| Burning rate | 60 | mm/min | ISO 3795 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Unnotch Impact strength | |||
| 23℃ | 110 | kJ/m² | ISO 179/1eU |
| -30℃ | 90 | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength | |||
| 23℃ | 15 | kJ/m² | ISO 179/1eA |
| -30℃ | 7 | kJ/m² | ISO 179/1eA |
| Impact strength of cantilever beam notch | |||
| 23℃ | 15 | kJ/m² | ISO 180-1A |
| -30℃ | 7 | kJ/m² | ISO 180-1A |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 110 | MPa | ISO 2039-1 |
| tensile strength | |||
| Yield, 23 ℃ | 46 | MPa | ISO 527-2 |
| Tensile strain | |||
| Yield, 23 ℃ | 2.6 | % | ISO 527-2 |
| Fracture, 23 ℃ | >=15 | % | ISO 527-2 |
| Tensile modulus | |||
| 23℃ | 2400 | MPa | ISO 527-2 |
| bending strength | |||
| 23℃ | 70 | MPa | ISO 178 |
| Bending modulus | |||
| 23℃ | 2400 | MPa | ISO 178 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2 mm |
| 3. 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Rate A (50°C/h), Loading 2 (50 N) |
| 7. US-FMVSS |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |