| About |
|---|
| Elix ABS M220 General purpose grade for self coloring&& |
| Product Description | |
|---|---|
| Generic | ABS |
| Material Status | Commercial: Active |
| Features | Good coloring |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 25℃ | 1.05 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 11 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 220℃，10 kg | 32.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.60 | % | |
| MD | 0.60 | % | |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30℃ | 11 | kJ/m² | |
| 23℃ | 18 | kJ/m² | |
| Charpy Unnotch Impact strength | |||
| -30℃ | 80 | kJ/m² | |
| 23℃ | 100 | kJ/m² | |
| Impact strength of cantilever beam notch | |||
| -30℃，3.2mm | 120 | J/m | ASTM D256 |
| 23℃，3.2mm | 230 | J/m | ASTM D256 |
| 23℃，6.4mm | 180 | J/m | ASTM D256 |
| -30℃ | 12 | kJ/m² | ISO 180-1A |
| 23℃ | 18 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 97.0 | ℃ | ISO 75-2/B |
| 1.8 MPa, annealed | 92.0 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 95.0 | ℃ | ASTM D1525 6 |
| B120 | 97.0 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 1.0E-4 | 1/℃ | |
| TD：23~55℃ | 1.0E-4 | 1/℃ |
| Electrical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| Surface resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Dielectric strength | |||
| 1 mm | 35 | kV/mm | IEC 60243-1 |
| Relative permittivity | |||
| 100 Hz | 2.90 | ||
| 1 MHz | 2.90 | ||
| Dissipation factor | |||
| 100 Hz | 7.3E-3 | ||
| 1 MHz | 9.0E-3 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Ball hardness | 103 | MPa | ISO 2039-1 |
| Tensile modulus | |||
| — | 2300 | MPa | ASTM D638 |
| — | 2300 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 37.9 | MPa | ASTM D638 |
| yield | 41.0 | MPa | ISO 527-2/50 |
| Bending modulus | |||
| — | 2200 | MPa | ASTM D790 |
| — | 2200 | MPa | ISO 178 |
| bending strength | 65.0 | MPa | ISO 178 |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 240 | °C | |
| Mold temperature | 80 | °C | |
| Injection Velocity | 14 | m/min | ISO 294 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2 mm |
| 3. 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Rate A (50°C/h), Loading 2 (50 N) |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |