| PC/ABS blend, injection molding grade that poses a good combination of impact, stiffness and toughness. Vicat B120 = 130°C Benefits: Easy Flow Very high impact up to -40°C Low emission grade UV stabilized grade Good stability even with high humidity conditions Low shrinkage Good paintability Thin-walled parts Chemical Composition: Thermoplastic polymer blend based on polycarbonate (PC) and acrylonitrile-butadiene-styrene (ABS).&& |
| Product Description | |
|---|---|
| Generic | PC+ABS |
| Material Status | Commercial: Active |
| Features | Weather resistance is good,High impact resistance,Good liquidity,Sprayable,Low contractility,Low odor,Good stability |
| Availabilitys | North America,Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | |||
| 25℃ | 1.13 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，3.80kg | 4.0 | g/10min | ASTM D1238 |
| Melt Volume Rate | |||
| 260℃，5 kg | 21.0 | cm³/10min | ISO 1133 |
| Shrinkage rate | |||
| TD | 0.65 to 0.75 | % | |
| MD | 0.65 to 0.75 | % | |
| Water absorption rate | |||
| Saturation, 23 ℃ | 0.70 | % | |
| Equilibrium, 23 ℃, 50% RH | 0.20 | % | |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | |||
| — | 2270 | MPa | ASTM D638 |
| — | 2270 | MPa | ISO 527-1-2 |
| tensile strength | |||
| yield | 49.0 | MPa | ASTM D638 |
| yield | 52.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| fracture | 28 | % | ASTM D638 |
| fracture | 28 | % | ISO 527-2/50 |
| Bending modulus | |||
| — | 2280 | MPa | ASTM D790 |
| — | 2280 | MPa | ISO 178 |
| bending strength | 85.0 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| -30℃，3.2mm | 490 | J/m | ASTM D256 |
| 23℃，3.2mm | 580 | J/m | ASTM D256 |
| 23℃，6.4mm | 440 | J/m | ASTM D256 |
| -40℃ | 30 | kJ/m² | ISO 180-1A |
| -30℃ | 39 | kJ/m² | ISO 180-1A |
| 23℃ | 53 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, annealed | 123 | ℃ | ISO 75-2/B |
| 1.8 MPa, annealed | 104 | ℃ | ISO 75-2/A |
| Vicat Softening Temp | |||
| — | 128 | ℃ | ASTM D1525 6 |
| B120 | 130 | ℃ | ISO 306/B120 |
| Linear coefficient of thermal expansion | |||
| MD：23~55℃ | 7.7E-5 | 1/℃ | |
| TD：23~55℃ | 8.1E-5 | 1/℃ |
| FLAME CHARACTERISTICS | Nominal value | Unit | Test method |
|---|---|---|---|
| 1.60 mm | HB | UL 94 | |
| Burning rate | |||
| 2.0 mm | < 80 | mm/min | ISO 3795 |
| carbon emission | |||
| 23℃ | < 15.0 | µgC/g | VDA 277 |
| Supplementary information | Nominal value | Unit | Test method |
|---|---|---|---|
| discharge | |||
| FOG：23℃ | < 10.0 | µg/g | |
| VOC：23℃ | < 10.0 | µg/g |
| Process Conditions | |||
|---|---|---|---|
| injection | Nominal value | Unit | Test method |
| Processing (melt) temperature | 260 | °C | |
| Mold temperature | 80 | °C | |
| Injection Velocity | 14 | m/min | ISO 294 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 60x60x2 mm |
| 3. 0.20 in/min |
| 4. 0.051 in/min |
| 5. 0.079 in/min |
| 6. Rate A (50°C/h), Loading 2 (50 N) |
| 7. US-FMVSS |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |