| ELTEX® MED 100-MG03 is a non-nucleated polypropylene homopolymer intended for injection moulding, extrusion and thermoforming converting processes requiring medium melt flow and good parison strength. ELTEX® MED 100-MG03 is produced according to Good Manufacturing Practices, and is available in granular form. Applications ELTEX® MED 100-MG03 is especially recommended for manufacturing dry powder / metered dose inhaler components by injection moulding. It can also be used for primary rigid packaging of medical and pharmaceutical applications.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Low Residuals,Optical performance,Low odor,Moderate liquidity,Block resin,Homopolymer |
| Availabilitys | Europe |
| Process Methods | Thermo forming |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Melt Flow Rate | |||
| 230℃，2.16kg | 3.0 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| tensile strength | |||
| yield | 35.0 | MPa | ISO 527-2 |
| Bending modulus | |||
| 23℃ | 1450 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Impact strength of cantilever beam notch | |||
| 23℃ | 4.0 | kJ/m² | ISO 180-1A |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 93.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 156 | ℃ | ISO 306/A |
| Melting peak temperature | 163 | ℃ | ASTM D3418 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2nd heating |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |