Eltex® MED PH27D630

About
Low Density Polyethylene for Pharmaceutical Blow Moulding Benefits & Features Eltex® MED PH27D630 is a LD-polyethylene produced in a high-pressure process intended for blow moulding of soft and flexible packages for pharmaceutical products. Eltex® MED PH27D630 is produced according to good manufacturing practice and is additive-free. Eltex® MED PH27D630 is available in granular form. Applications Eltex® MED PH27D630 can be used in “blow-fill and seal” machines for the production ampoules and bottles. The product can also be used for pharmaceutical products manufactured with other conversion techniques such as injection moulding and film blowing. Eltex® MED PH27D630 will withstand heating up to 110°C and therefore units made from this product may be steam treated to max. 110°C.&&

About

Low Density Polyethylene for Pharmaceutical Blow Moulding Benefits & Features Eltex® MED PH27D630 is a LD-polyethylene produced in a high-pressure process intended for blow moulding of soft and flexible packages for pharmaceutical products. Eltex® MED PH27D630 is produced according to good manufacturing practice and is additive-free. Eltex® MED PH27D630 is available in granular form. Applications Eltex® MED PH27D630 can be used in “blow-fill and seal” machines for the production ampoules and bottles. The product can also be used for pharmaceutical products manufactured with other conversion techniques such as injection moulding and film blowing. Eltex® MED PH27D630 will withstand heating up to 110°C and therefore units made from this product may be steam treated to max. 110°C.&&

Product Description
Supplier	INEOS
Generic	LDPE
Material Status	Commercial: Active
Features	Good flexibility,Steam sterilized,Low density,Soft
Availabilitys	Europe

Technical Data
PHYSICAL	Nominal value	Unit	Test method
Density	0.927	g/cm³	ISO 1183
Melt Flow Rate
190℃，2.16kg	0.30	g/10min	ISO 1133

MECHANICAL	Nominal value	Unit	Test method
Shore hardness
Shaw’s D	52		ISO 868
Tensile modulus	350	MPa	ISO 527-1-2
tensile strength
yield	12.0	MPa	ISO 527-2/50
Tensile strain
fracture	350	%	ISO 527-2/50

THERMAL	Nominal value	Unit	Test method
Hot deformation temperature
0.45 MPa, unannealed	51.0	℃	ISO 75-2/B

Process Conditions
Extrusion	Nominal value	Unit	Test method
Melt temperature	165 to 200	°C

Notes
【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.

Notes

【 Disclaimer 】
Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials.