| Eltex® PF6212KJ is a metallocene LLDPE grade produced in Europe Benefits & Features Eltex® PF6212KJ is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties: Extremely high impact strength Excellent optical properties Very good bubble stability and extrudability Low temperature sealing characteristics Applications Eltex® PF6212KJ has been developed for use in food packaging and other thin film applications where excellent mechanical and optical performance is required. For more demanding applications such as lamination and temporary surface protection, we recommend to use Eltex® PF6212LJ If corona treatment is necessary, the level should normally be in the range 38-48 mN/m.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | Excellent Processability,High impact resistance,Smoothness,Optical performance,High anti-blocking,Food contact compliance,Inoxidizability,Low density,Copolymer,Hexene copolymers,Low temperature heat sealing |
| Availabilitys | Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.920 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 1.3 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| friction coefficient | |||
| Blown film | < 0.25 | ASTM D1894 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, 25 µ m, blow molded film | 180 | MPa | ISO 527-3 |
| 1% secant, TD, 25 µ m, blow molded film | 200 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 25 µ m, blow molded film | 9.00 | MPa | ISO 527-3 |
| TD, yield, 25 µ m, blow molded film | 10.0 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 65.0 | MPa | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 60.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 550 | % | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 670 | % | ISO 527-3 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | > 1000 | g | ASTM D1709-A |
| tear strength | |||
| TD, 25 µ m, blow molded film | 440 | g | ASTM D1922 |
| MD, 25 µ m, blow molded film | 200 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 105 to 118 | ℃ | ASTM D3418 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 62 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 8.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 230 | °C | |
| Notes |
|---|
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |