| Benefits & Features Eltex® PF6220AA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties: High impact strength and rigidity Excellent optical properties Very good bubble stability and extrudability similar to the best LLDPE blown film grades Low temperature sealing characteristics Applications Eltex® PF6220AA has been developed for use in collation shrinkwrap, food packaging and other thin film applications where an excellent balance between film strength and rigidity is required together with good optical properties. In addition, Eltex® PF6220AA offers easy extrudability. If corona treatment is necessary, the level should be in the range 38-48 mN/m.&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | mLLDPE |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,High impact resistance,Optical performance,Food contact compliance,Inoxidizability,Low density,Copolymer,Hexene copolymers,Low temperature heat sealing |
| Availabilitys | Europe |
| Process Methods | Film extrusion |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.919 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 190℃，2.16kg | 2.1 | g/10min | ISO 1133 |
| film | Nominal value | Unit | Test method |
|---|---|---|---|
| film thickness | |||
| test | 25 | µm | |
| Tensile modulus | ISO 527-3 | ||
| 1% secant, MD, 25 µ m, blow molded film | 160 | MPa | ISO 527-3 |
| 1% secant, TD, 25 µ m, blow molded film | 195 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, yield, 25 µ m, blow molded film | 9.00 | MPa | ISO 527-3 |
| TD, yield, 25 µ m, blow molded film | 10.0 | MPa | ISO 527-3 |
| tensile strength | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 60.0 | MPa | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 60.0 | MPa | ISO 527-3 |
| Tensile strain | ISO 527-3 | ||
| MD, fracture, 25 µ m, blow molded film | 620 | % | ISO 527-3 |
| TD, fracture, 25 µ m, blow molded film | 700 | % | ISO 527-3 |
| Drop hammer impact | |||
| 25 µ m, blow molded film | 1000 | g | ASTM D1709-A |
| tear strength | |||
| TD, 25 µ m, blow molded film | 450 | g | ASTM D1922 |
| MD, 25 µ m, blow molded film | 220 | g | ASTM D1922 |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Melting peak temperature | 104 to 116 | ℃ | ASTM D3418 |
| optical performance | Nominal value | Unit | Test method |
|---|---|---|---|
| gloss | |||
| 45 °, 25 µ m, blow molded film | 60 | ASTM D2457 | |
| Haze | |||
| 25 µ m, blow molded film | 8.0 | % | ASTM D1003 |
| Process Conditions | |||
|---|---|---|---|
| Extrusion | Nominal value | Unit | Test method |
| Melt temperature | 190 to 230 | °C | |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. 2nd heating |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |