| About |
|---|
| Eltex TUB 433-NA00 is a low melt flow rate, long term heat stabilized, high impact copolymer for pipe, blow moulding and sheet extrusion applications. It offers a very good balance stiffness – impact strength (even at low temperature) and excellent processability. Applications: Non-pressure pipes / fittings Blow moulding Sheet extrusion Benefits and Features: High impact resistance Good rigidity Excellent melt strength Long term heat stability Excellent processability (for solid and structured wall pipes extrusion)&& |
| Product Description | |
|---|---|
| Supplier | INEOS |
| Generic | PP homopolymerization |
| Material Status | Commercial: Active |
| Features | Good Rigidity,Excellent Processability,Low liquidity,High impact resistance,Good melt strength,low-temperature impact resistance,Impact copolymer,Heat Stabilized |
| Availabilitys | Europe |
| Technical Data | |||
|---|---|---|---|
| PHYSICAL | Nominal value | Unit | Test method |
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| 230℃，2.16kg | 0.30 | g/10min | ISO 1133 |
| MECHANICAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Tensile modulus | 1500 | MPa | |
| tensile strength | |||
| Yield, 23 ℃, 4.00 mm, injection molding | 28.0 | MPa | ISO 527-2/50 |
| Tensile strain | |||
| Yield, 23 ℃, 4 mm, injection molding | 9.0 | % | ISO 527-2/50 |
| Bending modulus | |||
| 23 ℃, 4 mm, molded | 1500 | MPa | ISO 178 |
| IMPACT | Nominal value | Unit | Test method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20 ℃, injection molding | 7.0 | kJ/m² | ISO 179/1eA |
| 0 ℃, injection molding | 18 | kJ/m² | ISO 179/1eA |
| 23 ℃, injection molding | > 50 | kJ/m² | ISO 179/1eA |
| THERMAL | Nominal value | Unit | Test method |
|---|---|---|---|
| Hot deformation temperature | |||
| 0.45 MPa, unannealed | 95.0 | ℃ | ISO 75-2/B |
| Vicat Softening Temp | 155 | ℃ | ISO 306/A |
| Melting temperature | 165 | ℃ | ASTM D3417 |
| Oxygen sensing time | |||
| 200℃ | > 30 | min | DIN EN 728 |
| Notes |
|---|
| 1. Typical properties: these are not to be construed as specifications. |
| 2. Calculated from ring stiffness measurements carried out on 110 mm solid wall pipes |
| 3. Cooling Rate = -15°C/min |
| 4. 4 mm thickness |
| 【 Disclaimer 】 Guangzhou Soliao Information Technology Co., Ltd. reserves all rights. The information in this data table was obtained from the manufacturer of the material on soliao.com. Soliao.com makes every effort to ensure the accuracy of this data. However, the search company does not assume any responsibility for the uncertainty and consequences caused to users by these data values and suggestions, and strongly recommends verifying the data values with the material supplier before the final selection of materials. |